products details

Home > Products >

3D Multilayer Zirconia

Low-Temp Sintered Zirconia Disc ≤3-Unit Prosthesis 1150-1250 HV10 <0.1 Bq/g Radioactivity

All Category

Other Dental Equipment

Miss. Seratina

seratina.zeng@leomedtech.com

+8618883956206

Contact Now

Low-Temp Sintered Zirconia Disc ≤3-Unit Prosthesis 1150-1250 HV10 <0.1 Bq/g Radioactivity

Brand Name:	LEOTECH
Model Number:	UT-ML
MOQ:	500 pcs
Price:	$69.44/piece
Payment Terms:	T/T

Detail Information

Product Description

Detail Information

Place of Origin:

Chongqing, China

Certification:

Product Name:

UT-ML Dental Zirconia Block

Product Specification:

98, 95, 92*75*30 Mm

Thickness:

30 Mm

Price:

69.44

Power Source:

Manual

Warranty:

1 Year

After-sale Service:

Online Technical Support

Quality Certification:

Instrument Classification:

Class II

Color:

16 VITA Classical

Highlight:

Low-Temp Sintered Zirconia Disc

1150-1250 HV10 Zirconia Disc

Product Description

Low-Temp Sintered Zirconia Disc ≤3-Unit Prosthesis 1150-1250 HV10 <0.1 Bq/g Radioactivity

UT-ML Dental Zirconia Block

● High Strength ● High Transparency ● Natural

Low-Temp Sintered Zirconia Disc ≤3-Unit Prosthesis 1150-1250 HV10 <0.1 Bq/g Radioactivity 0

UT-ML Multilayer Zirconia: Technical Profile

Composition: ≥99% purity, 8.0–10.0% $Y_{2} O_{3}$
Properties:
- Translucency: 49–53% (1.0 mm)
- Flexural Strength: 600–800 MPa
- Hardness: 1150–1250 HV10
Safety: 0 cytotoxicity | <0.1 Bq/g radioactivity
Applications: Single crowns & 3-unit bridges
Sintering: 1500°C (1480–1510°C)

Product Parameters:

Model	UT Multilayer 95mm
Size	95mm
Strength	600-800 MPa
Shades	16 VITA Classical.
Disc Sizes	9 thicknesses(10,12.14.16.18.20.22.25.30mm)

Technical Parameters:

1.Chemical composition

Components	UT-ML
ZrO2+HfO2+Y2O3	≥99%
Y2O3	8.0%-10.0%
Al2O3	＜0.15%
Other Oxides	＜0.5%

2.Physical characteristics

Properties	UT-ML
Density before sintering(g.cm-3)	3.15±0.05
Density after sintering(g.cm-3)	6.06±0.02
CTE(25-500℃)(K-1)	(10.5±0.5)×10-6
Flexural strength after sintering(Mpa)	600-800
Translucency(1.0±0.02mm)	49%-53%
Fracture toughness(MPa.m1/2)	3.5-5.0
Hardness(HV10)	1150-1250
Accelerated aging surface monoclinic phase content	＜5%
Chemical solubility after sintering(μg.cm-2)	＜100
Cytotoxicity	0 Level
Radioactivity(Bq.g-1)	＜0.1
Sintering temperature(℃)	1480-1510 Recommend 1500