products details

Home Products

Yttria-Stabilized Zirconia Blank / 10.5×10⁻⁶/K Thermal Expansion / ≤3-Unit Bridges | HV10 1150-1250

Name: Yttria-Stabilized Zirconia Blank / 10.5×10⁻⁶/K Thermal Expansion / ≤3-Unit Bridges | HV10 1150-1250
Brand: Chongqing Leomed Technology Co., Ltd.
SKU: UT-ML
Price: 31.94 USD
Availability: InStock

Brand Name:	LEOTECH
Model Number:	UT-ML
MOQ:	500 pcs
Price:	$31.94/piece
Payment Terms:	T/T

Detail Information

Product Description

Detail Information

Place of Origin:

Chongqing, China

Certification:

Product Name:

UT-ML Dental Zirconia Block

Product Specification:

98, 95, 92*75*12 Mm

Thickness:

12 Mm

Price:

31.94

Power Source:

Manual

Warranty:

1 Year

After-sale Service:

Online Technical Support

Shelf Life:

1 Year

Quality Certification:

Instrument Classification:

Class II

Highlight:

10.5×10⁻⁶/K Yttria Stabilized Zirconia Blank

HV10 1150-1250 Yttria Stabilized Zirconia Blank

Product Description

Yttria-Stabilized Zirconia Blank 10.5×10⁻⁶/K Thermal Expansion ≤3-Unit Bridges HV10 1150-1250

UT-ML Dental Zirconia Block

● High Strength ● High Transparency ● Natural

Yttria-Stabilized Zirconia Blank / 10.5×10⁻⁶/K Thermal Expansion / ≤3-Unit Bridges | HV10 1150-1250 0

UT-ML: Aesthetic & Durable Dental Zirconia
Achieve natural aesthetics with 49–53% translucency and multilayer effects. Exceptional strength (800 MPa) ensures longevity for crowns and 3-unit bridges. Biocompatible (0 cytotoxicity) and low radioactivity (<0.1 Bq/g). Monoclinic phase <5% post-aging guarantees stability.

Product Parameters:

Model	UT Multilayer 95mm
Size	95mm
Strength	600-800 MPa
Shades	16 VITA Classical.
Disc Sizes	9 thicknesses(10,12.14.16.18.20.22.25.30mm)

Technical Parameters:

1.Chemical composition

Components	UT-ML
ZrO2+HfO2+Y2O3	≥99%
Y2O3	8.0%-10.0%
Al2O3	＜0.15%
Other Oxides	＜0.5%

2.Physical characteristics

Properties	UT-ML
Density before sintering(g.cm-3)	3.15±0.05
Density after sintering(g.cm-3)	6.06±0.02
CTE(25-500℃)(K-1)	(10.5±0.5)×10-6
Flexural strength after sintering(Mpa)	600-800
Translucency(1.0±0.02mm)	49%-53%
Fracture toughness(MPa.m1/2)	3.5-5.0
Hardness(HV10)	1150-1250
Accelerated aging surface monoclinic phase content	＜5%
Chemical solubility after sintering(μg.cm-2)	＜100
Cytotoxicity	0 Level
Radioactivity(Bq.g-1)	＜0.1
Sintering temperature(℃)	1480-1510 Recommend 1500

Indications For Use ≤3 units

Yttria-Stabilized Zirconia Blank / 10.5×10⁻⁶/K Thermal Expansion / ≤3-Unit Bridges | HV10 1150-1250 2

Sintering:

Factory Display:

Application:

Exhibition:

Tags:

3-Unit Bridges Zirconia

Low Temperature Sintering Zirconia

UT ML Dental Zirconia Blank

Manual Lithium Disilicate Glass Dental Material Cerec CAD CAM C14 Block For Cerec

Get Best Price

A1 - A4 Lithium Disilicate Glass Natural Looking Esthetics Lithium Disilicate In Dentistry

Get Best Price

360Mpa ~ 400Mpa Class II Dental Lithium Disilicate Zirconia Glass Ceramic

Get Best Price

Video

4D 3D Multilayer Zirconia 92 X 75MM Dental Zirconia Block Rectangle Shape

Get Best Price

Video

Multi Color Multilayer Zirconia Block Personalized Tooth Whitening Restoration Zircon Multilayer

Get Best Price

Video

Class II 92mm Multilayer Zirconia Medical Instrument Zirconia Dental Block

Get Best Price

Video

98mm Manual 3D Multilayer Zirconia Blocks Dental 10MM - 30MM Thickness

Get Best Price

Video

B1 B2 Colours SHT Zirconia Multilayer Block For Veneers Teeth

Get Best Price

CE Certified Dental Zirconia Block Class II Instrument Classification

Get Best Price

Onlay Indications ST Multilayer Zirconia with 16 Shades and Sintering Temperature of 1530C

Get Best Price

Class II Instruments Dental Zirconia Block With And Fracture Toughness 5 MPa·m1/2

Get Best Price

1530C Sintering Temperature ST Multilayer Zirconia With 16 Shade Options 42% Translucency

Get Best Price

Products Details

Home Products

Zirconia Material

Yttria-Stabilized Zirconia Blank / 10.5×10⁻⁶/K Thermal Expansion / ≤3-Unit Bridges | HV10 1150-1250

All Category

Zirconia Material

3D Multilayer Zirconia

SHT Multilayer Zirconia

SHT Color Zirconia

SHT White Zirconia

ST Multilayer Zirconia

ST White Zirconia

ST Color Zirconia

HT Zirconia

Lithium Disilicate

Other Dental Materials

Dental Equipment

Dental Scanner

Dental Milling Machines

Dental Sintering Furnace

Dental Porcelain Furnace

Dental 3D Printer

Dental Consumables

3D Printing Materials

Clinic Products

Other Dental Equipment

Yttria-Stabilized Zirconia Blank / 10.5×10⁻⁶/K Thermal Expansion / ≤3-Unit Bridges | HV10 1150-1250

Brand Name:	LEOTECH
Model Number:	UT-ML
MOQ:	500 pcs
Price:	$31.94/piece
Payment Terms:	T/T

Detail Information

Product Description

Detail Information

Place of Origin:

Chongqing, China

Brand Name:

LEOTECH

Certification:

Model Number:

UT-ML

Product Name:

UT-ML Dental Zirconia Block

Product Specification:

98, 95, 92*75*12 Mm

Thickness:

12 Mm

Price:

31.94

Power Source:

Manual

Warranty:

1 Year

After-sale Service:

Online Technical Support

Shelf Life:

1 Year

Quality Certification:

Instrument Classification:

Class II

Minimum Order Quantity:

500 pcs

Price:

$31.94/piece

Payment Terms:

T/T

Highlight:

10.5×10⁻⁶/K Yttria Stabilized Zirconia Blank

HV10 1150-1250 Yttria Stabilized Zirconia Blank

Product Description

Yttria-Stabilized Zirconia Blank 10.5×10⁻⁶/K Thermal Expansion ≤3-Unit Bridges HV10 1150-1250

UT-ML Dental Zirconia Block

● High Strength ● High Transparency ● Natural

Yttria-Stabilized Zirconia Blank / 10.5×10⁻⁶/K Thermal Expansion / ≤3-Unit Bridges | HV10 1150-1250 0

Product Parameters:

Model	UT Multilayer 95mm
Size	95mm
Strength	600-800 MPa
Shades	16 VITA Classical.
Disc Sizes	9 thicknesses(10,12.14.16.18.20.22.25.30mm)

Technical Parameters:

1.Chemical composition

Components	UT-ML
ZrO2+HfO2+Y2O3	≥99%
Y2O3	8.0%-10.0%
Al2O3	＜0.15%
Other Oxides	＜0.5%

2.Physical characteristics

Properties	UT-ML
Density before sintering(g.cm-3)	3.15±0.05
Density after sintering(g.cm-3)	6.06±0.02
CTE(25-500℃)(K-1)	(10.5±0.5)×10-6
Flexural strength after sintering(Mpa)	600-800
Translucency(1.0±0.02mm)	49%-53%
Fracture toughness(MPa.m1/2)	3.5-5.0
Hardness(HV10)	1150-1250
Accelerated aging surface monoclinic phase content	＜5%
Chemical solubility after sintering(μg.cm-2)	＜100
Cytotoxicity	0 Level
Radioactivity(Bq.g-1)	＜0.1
Sintering temperature(℃)	1480-1510 Recommend 1500

Indications For Use ≤3 units

Yttria-Stabilized Zirconia Blank / 10.5×10⁻⁶/K Thermal Expansion / ≤3-Unit Bridges | HV10 1150-1250 2

Sintering:

Factory Display:

Application:

Exhibition:

Tags: